[Hot Item] Catalyst Carrier Ceramic Honeycomb Substrate Honeycomb Ceramic Support

Basic Info.

Model NO.

CHS

Certification

ISO9001

Component

Catalytic Converter

Material

Cordierite

Common Specification

Diameter<120mm/Diameter<200mm,etc

Transport Package

Wooden Box and Pallet/Packed as Customers' Need

Origin

China

HS Code

6909190000

Production Capacity

100, 000pieces/Month

Product Description

Ceramic substrate 20/40 process bauxite with high content finely and make it into small and round grains with different grain diameters like 0.45mm-0.90mm, 0.09mm-0.224mm with chemical agents and transformation agents. Finally fire them under high temperature. In this way, high strength fracturing propping agent is finished. It has high strength, low breaking rate, good sphericity, etc. Under closing pressure. It is the best product for stratum fracturing transformation of oil and gas field at present.
After coated with catalysts, this product is applied in catalytic converter of diesel vehicle to catalyze, convert and purify the exhaust, making vehicle exhaust reaching standards of Euro IV and Euro V. Technical performance of the product in the leading position in domestic, close to or reach the advanced level of similar foreign product.

Catalyst Carrier Ceramic Honeycomb Substrate Honeycomb Ceramic Support

Catalyst Carrier Ceramic Honeycomb Substrate Honeycomb Ceramic Support

Ceramic Substrate Usage
It is mainly used for supporting fissure of stratum fracturing transformation of deep oil and gas field.
Enhance permeability of stratum Circulate oil gas.
Increase output of oil gas.
*Low thermal expansion coefficient
*High porosity of hole on the wall, good liquidity and uniform distribution.
*High temperature resistance, chemical corrosion resistance, thermal shock resistance and thermal shock resistance is strong.
*The pressure drop is small.
*Cold start performance is good, low light-off temperature, high conversion efficiency.

Catalyst Carrier Ceramic Honeycomb Substrate Honeycomb Ceramic Support

Item		Standard values	Test method
Wall thinkness	100CPSI	0.45MM±0.03	vernier caliper
	200CPSI	0.36MM±0.03	vernier caliper
	300CPSI	0.28MM±0.03	vernier caliper
	400CPSI	0.21MM ±0.03	vernier caliper
Overall dimensions	OD:<100MM	±1.0MM	vernier caliper
	≥100MM	±1%	vernier caliper
	Height:<150	±1.0	vernier caliper
	≥150	±1%Height	vernier caliper
Internal crack			Bright light perspective

Item			Standard value	Test methods
chemical component	Al2O3		35.2%±1%	chemical analysis
	SiO2		50.9%±1%
	MgO		13.9%±1%
Cordierite main crystalline phase content			≥90%	X-ray diffraction
Compressive strength at room temperature		AA xis	≥15Mpa	universal material testing machine
		BB xis	≥2Mpa
		CC xis	≥0.15Mpa
water absorption			23-27%	Gravimetric method
softening temperature			≥1400 Degree C	high-temperature electric resistance furnace
CTE(800 Degree C)			≤1.5*10-6/Degree C	thermal dilatometer
thermal shock resistance			450 Degree C Three times don't crack	air cooling